DESCRIPTION | GK-MH can reduce surface defects, maintain the uniformity of surface colour, and improve the quality of the concrete surface. At the same time, it reduces the adhesion of concrete to the mold and thus leads to easy demolding. |
USES | GK-MH is suitable for steel mold, wood mold, plastic mold, plywood formwork, precast concrete and architectural concrete. |
CHARACTERISTICS | GK-MH offers the following advantages: * Reduce air voids on concrete surface and improves appearance of concrete (fair-faced concrete); * No migration to concrete surface and no negative effects in case of later coating; * Reduce repair cost; * Easy to demold; * No corrosion on reinforcement; * Good stability after dilution, and water will not separate from oil. |
PRODUCT DATA | Chemical Base | Polycarboxylate-ether |
| Appearance/Colour | Liquid/oyster white |
| Packaging | Barrel 225kg, IBC 1100kg or bulk transport |
| Storage conditions | Store in dry conditions, protected from direct sunlight, water and frost |
| Shelf-life | At least 6 months if stored properly. If expired, it can only be used after inspection. |
| Density (at 25℃) | 0.94—0.98 g/cm3 |
| pH Value (at 25°C) | 6—7 |
| Solid Content | ≥ 55% (See CoA for details) |
| Chloride Content | ≤ 0.1% |
| Alkali content | ≤ 0.3% |
Shotcrete Accelerators> GK-A3 High-Performance Stickine GK-3B WJ-1 Shotcrete Accelerato GK-3B WJ-1 Shotcrete Accelerato >>MoreWater reducing and slump retaining polymers> GK-FB Polycarboxylate Water Red GK-3000 Polycarboxylate based H GK-A Superplasticizer GK-4A Set Retarding Superplasti >>MoreFunctional additives> GK-2A Hardening Accelerating An GK-Z Concrete Anti-mud Agent GK-XP Defoamer GK-9A Air Entraining Admixture >>MoreFunctional materials> GK-4Z Inhibitor of Hydration He GK-ZMJ Grinding Agent GK-3Z Nanocrystalline Seed Acce GK-EPW Solvent-free Epoxy Resin GK-SR Surface Reinforcing Agent GK-3G Silane Impregnating Agent GK-I Synergist GK-20A Impact and Wear Resistan GK-8A Concrete Curing Agent GK-3D Shield Foaming Agent >>More